Objective To evaluate the feasibility and the value of the layered cylindric collagenhydroxyapatite composite as a scaffold for the cartilage tissue engineering after an observation of how it absorbs the chondrocytes and affe cts the cell behaviors. Methods The chondrocytes were isolated and multiplied in vitro, and then the chondrocytes were seeded onto the porous collagen／h ydro xyapatite composite scaffold and were cultured in a three-dimensional environme n t for 3 weeks. The effects of the composite scaffold on the cell adhesivity, proliferation, morphological changes, and synthesis of the extracellular matrix were observed by the phase-contrast microscopy, histology, scanning electron micros copy, and immunohistochemistry. Results The pore diameter of the upper layer of the collagen-hydroxyapatite composite scaffold was about 147 μm. and the porosity was 89%; the pore diameter of the bottom layer was about 85 μm and the porosity was 85%. The layered cylindric collagenhydroxyapatite composite scaffold had good hydrophilia. The chondrocytes that adhered to the surface of the scaffold, proliferated and migrated into the scaffold after 24 hours. The chondrocytesattached to the wall of the microholes of the scaffold maintained a rounded morphology and could secrete the extracellular matrix on the porous scaffold. Conclusion The layered cylindric collagenhydroxyapatite composite scaffold has a good cellular compatibility, and it is ber in the mechanical property than the pure collagen. It will be an ideal scaffold for the cartilage tissue enginee ring.
Objective To evaluate the biocompatibility and safety of a novel orthopedics materials-graded zirconia(ZrO2)hydroxyapatite(HA) composite biomaterials. Methods First, ultrafine powers of ZrO2 and HA powder were prepared by chemical precipitation method, then graded ZrO2-HA composite was synthesized by dry-laying and sintering method. After the physiological saline and culture medium extracts of the composite were prepared, four experiments were conducted as follows:① The mouse acute toxic test consists of 2 groups(n=10). The extracts were intravenously injected to mice in the first group, and physiological saline to mice in the second group. The dose was 50 g/kg. Their toxicity manifestation, morality and the change of weight were recorded.② The standard curve of proliferation and metabolism of L929 cells was established. ③ The cytotoxinic test consists of 3 groups: materials group (extracts of the materials), positive control group (culture fluid with 0.64% phenol), and negative control group (RPMI-1640 culture fluid). Each of three was cultured with cell suspension, and then the morphology of the cells was observed, the relative proliferation rate (RGR) was calculated, and the toxicity was classified. ④ In vitrohemolytic test was divided into 3 groups: extracts, sterile distilled water (positive control) and 0.9% physiological saline. In each of three, 0.2 ml anticoagulant diluted fresh rabbit blood was added. The percentage of hemolysis was tested. ⑤ The muscle and implantation test were divided into 4 groups(n=3). The composite biomaterials were implanted into pygal muscleson either side and lateral condyles of femurs. After surgery, the rats of four groups were sacrificed at 12 and 24 weeks respectively.Tissue slice and scanning electronic microscopy were performed. Results General acute toxic test: no mouse died within 3 weeks; no toxicity symptom or adverse effects were shown within 3 days. The weight of materials group increased by 3.57±0.49 g, and the control group by 3.62±0.61 g, showing no statistically significant difference（Ρgt;0.05）.The standard curve of L929 cell perliferation and metabolism showed that their existed a positive correlation between the number of L929 cells and the perliferation. ③ Cytotoxinic test: cytosomes in the positive control group diminished and appeared round, there were pyknotic nucleus, the attached cells agglomerated; the toxicity was level Ⅳ. The morphology of cells in materials groupand negative control group was normal, and the number of them increased; the toxicity was level Ⅰand level 0, respectively. The MTT color experiments showed that positive control group was significantly lower than materials group and negative control group, showing statistically significant difference (Plt;0.01); there was no statistically significant difference between materials group and negative group.④ Hemolytic test: in vitrohemolytic rate of negative control group was0, of positive control group was 100%, and of materials group was 1.66%, which accords with the standard that hemolytic rate should be lower than 5% specified in ISO. ⑤ Implant test:No apparent rejection reaction took place after the composite was implanted; the composite bonded with the bones of the receptors firmly, which had good bonedinduced effect. Conclusion Graded ZrO2-HA composite bioceramic has good biocompatibility and is suitable for orthopedic biomaterials.
The primary results of five patients in whomthe block hydroxyapatite artificial bone (BHAB)used in maxillofacial plastic repair were reported. All incisions healed up with no evidence ofinfection. None of the implants was rejected norhad resorption changes. Satisfactory estheticaleffects were maintained. The results demonst-rated BHAB had a good biocampatibility andcould be used as a bone graft substitute inmaxillofacial plastic repair. This kind of material could be carved and contoured ...
Objective To investigate and compare the osteogenic potential of three kinds of calcium phosphate ceramic as carriers for recombinant human bone morphogenetic protein-2(rhBMP-2) in vivo.Methods BCPceramics (HA,TCP,HA/TCP) impregnated with rhBMP-2 (experimental groups) and without rhBMP-2(control groups) were implanted into 6 muscles pockets on the dorsum of 3month-old Wistar rabbits. The rabbits were sacrificed 2, 4 and 8 weeks after implantation and bone induction was estimated by alkaline phosphatase(ALP) activity measurement. The implants were also examined histologically and histomorphometrically by HE staining and computerized graphical analysis. Results The ALPactivity of implants withrhBMP-2 was higher than that of control groups(P＜0.05), but there was no difference between 2 and 4 weeks in experimental groups. In all experimental groups,theimplants exhibited that new bone formation increased with the lapse of time. The amount of new bone formation is more in -HA/rhBMP-2 group than in the other two group in the 2nd and 4th weeks, but there was no difference between them (P＞0.05).In the 8th week, the amount of bone formation was most in HA/TCP with -rhBMP-2, and was more than that in the 2nd and 4th weeks. Whereas in control groups, there was only fibrous connective tissue. Conclusion HA/TCP- is a good carriers of rhBMP-2 and can be used as bone substitutes clinically.
OBJECTIVE: To study the effect of collagen/hydroxyapatite(CHA) instead of autogenous bone transplantation on repairing the mandibular defects. METHODS: Ten Chinese experimental minipigs were made 2 cm bone defects in diameter in the mandible. The experimental group was implanted CHA, while the control group was implanted autogenous bone. The basic parameters of bone dynamics were determined by bone metrology. RESULTS: There was remarkable difference between the two groups in the mean distance and mineralization apposition rate of double label bands marked by tetracycline(P lt; 0.05), while the mean osteoid seam width and mineralization lag time had no remarkable difference(P gt; 0.05). It suggested that CHA had good osteogenesis. The collagen in CHA offered the condition of bone mineralization, and the mineralization peak of experimental group was present at 4 weeks earlier than that of control group (8 weeks). CONCLUSION: CHA may be a substitute of autogenous bone transplantation in repairing the mandibular defects, and the second operation for offering the implanting bone is avoidable, therefore, CHA may be an ideal material to repair bone defects.
OBJECTIVE: To evaluate the clinical effect of drilling procedure following the hydroxyapatite orbital implantation. METHODS: From February 1996 to April 2000, 146 consecutive patients who received hydroxyapatite orbital implant were drilled and inserted a motility peg 6 to 16 months after hydroxyapatite implantation. Among them, there were 97 males and 49 females, aged from 18 to 60 years old, of the 146 motility pegs, 36 were sleeved pegs and 110 were nonsleeved. Goldman visual field analyzer was applied to measure the degree of artificial eye’s movement before and after drilling. RESULTS: Followed up for 1 to 40 months, no secondary infection occurred. The mobility of the prosthesis increased from (18.7 +/- 3.8) degrees preoperatively to (42.3 +/- 3.7) degrees postoperatively. CONCLUSION: The delayed drilling procedure and motility peg insertion improve the range of movement and the sensitivity of the artificial eye with a low rate of complications.
OBJECTIVE To confirm membrane-guided tissue regeneration in the healing course of segmental bone defects and study the mechanism. METHODS Segmental, 1 cm osteoperiosteal defects were produced in both radii of 12 rabbits. One side was covered with hydroxyapatite/polylactic acid(HA/PLA) membrane encapsulated as a tube. The contralateral side served as an untreated control. Healing courses were detected by radiographic and histologic examinations. RESULTS All control sides showed nonunion, whereas there were consistent healing pattern in test sides. CONCLUSION Membrane technique can promote bone regeneration.
OBJECTIVE: To investigate the ability of repairing bone defect with the compound of coralline hydroxyapatite porous (CHAP), fibrin sealant(FS) and staphylococcus aureus injection (SAI), and the feasibility to use the compounds as bone substitute material. METHODS: The animal model of bone defect was made on the bilateral radius of 54 New Zealand white rabbits, which were randomly divided into the experimental group(the defect was repaired with CHAP-FS-SAI), control group(with autograft) and blank control group(the defect was left unrepaired) with 18 rabbits in each group. The ability of bone defect repair was evaluated by gross observation, histopathological study, X-ray and biomechanical analysis 2, 4, 8 and 12 weeks after repair. RESULTS: (1) In the 2nd week, tight fibro-connection could be found between the implant and fracture site and there were many fibroblasts and capillary proliferation with many chondrocytes around CHAP in the experimental group, while only a few callus formed, and chondrocytes, osteoblast and osteoclast existed in the control group. (2) In experimental group and control group, a large quantity of callus was found 4 and 8 weeks; ossification of chondrocytes with weave bone formation were found 4 weeks and many osteocytes and weave bones and laminar bones were found 8 weeks. (3) In the 12th week, the complete ossification of implant with well bone remodeling, a large number of mature osteocytes and laminar were found in experimental group and control group, and CHAP still existed in the experimental group; the defect area filled with fibro-scar tissue and only many fibroblasts could be seen in blank control group. (4) X-ray findings were the following: In experimental and control groups, callus formation could be seen 2 weeks postoperatively, more callus formed 4 weeks, the bone defect area disappeared and CHAP scattered in the callus 8 weeks; the fracture line disappeared and medullary cavity became united (in control group); and in the 12th week, the cortex became continuous, the medullary cavity became united, and remodeling completed, while bone defect was not still united in blank control group. The maximal torque and torsional stiffness in the experimental group is higher than those in the control group 2 weeks (P lt; 0.05), but there was no significant difference (P gt; 0.05) between the two groups 4, 8, 12 weeks after repair. CONCLUSION: The compound of CHAP-FS-SAI has good biological compatibility, and it can be used for one kind of bone substitute material to repair the bone defect.
Objective To investigate the effect of tissue engineering bone compounded in vitro by nanohydroxyapatite/collagen/ polylactic acid (nHAC/PLA) and recombinant human bone morphogenetic protein 2 (rhBMP-2) in repairing rabbit critical calvarial defects. Methods Forty eight New Zealand rabbits, weighting 2.0-2.5 kg, were made the models of critical cranial defects(15 mm in diameter) and divided into 4 groups randomly. Defects were repaired with autoflank bone in the positive control group; with no implant in the blank control group; with nHAC/PLA in the negative control; and with active nHAC/PLA(AnHAC/PLA) in the experimental group(the average quality of each AnHAC/PLA absorbed rhBMP-2 was 1.431 mg). The reapir results were observed through X-ray,HE dyeing and Masson’s trichrism dyeing after 8 and 16 weeks. Results The difference of bone formation was observed by X-ray block degree of skull defect area at 8 and 16 weeks. In the 8 th week and 16 th week, the radiopacities on cranial defect were 67.21%±2.06% and 86.48%±1.73% in the positive control group； 5.84%±1.92% and 9.48%±2.72% in the blank control group; 19.13%±2.51% and 35.67%±3.28% in the negative control group; and 58.84%±2.55% and 8561%±3.36% in the experimental group. There were significant differences between the negative control and the positive control group, and between the experimental group and the positive control group at 8 weeks(Plt;0.05) . There were significant differences between the negative control and blank group, and between the experiment and the blank group at 8 and 16 weeks(P＜0.05). The histology observation showed that the width of bone trabecula at 16 weeks was more than that at 8 weeks and bone defectwas full of bone tissue in positive control group. The bone defect was full of fibrous tissue at 8 and 16 weeks, and there was no new bone in the blank group. The bone defect was full of remnant material and fibrous tissue in the negative control group. The implanted area was replaced by the new bone at 8 weeks and the new bone was lamellar at 16 weeks in the experimental group; the residual material was less in defect area and there were more osteoblasts surrounding. Conclusion The nHAC/PLA is a good scaffoldmaterial of rhBMP-2 and AnHAC/PLA has agood ability in repairing bone defect. So it is hopeful to be applied in the clnical repair of large bone defect.