Objective To introduce the application of polymer material, chitosan, in the cartilage tissue engineering. Methods The recent original articleson the application of chitosan in cartilage tissue engineering were extensivelyreviewed. The biocompatibility and biodegradation characters of chitosan and its application were analysed.Results Chitosan has a high degree of biocompatibility and a favorable chondrogenic characteristic. It can support the maintenance of the phenotypic morphology of chondrocytes besides being used as a scaffold for cell growth. Conclusion The perspect of the application of chitosan in cartilage tissue engineering is hopeful.
【Abstract】 Objective To develop a novel cartilage acellular matrix (CACM) scaffold and to investigate its performance for cartilage tissue engineering. Methods Human cartilage microfilaments about 100 nm-5 μm were prepared after pulverization and gradient centrifugation and made into 3% suspension after acellularization treatment. After placing the suspension into moulds, 3-D porous CACM scaffolds were fabricated using a simple freeze-drying method. The scaffolds were cross-l inked by exposure to ultraviolet radiation and immersion in a carbodiimide solution 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide hydrochloride and N-hydroxysucinimide. The scaffolds were investigated by histological staining, SEM observation and porosity measurement, water absorption rate analysis. MTT test was also done to assess cytotoxicity of the scaffolds. After induced by conditioned medium including TGF-β1, canine BMSCs were seeded into the scaffold. Cell prol iferation and differentiation were analyzed using inverted microscope and SEM. Results The histological staining showed that there are no chondrocytefragments in the scaffolds and that toluidine blue, safranin O and anti-collagen II immunohistochemistry staining werepositive. The novel 3-D porous CACM scaffold had good pore interconnectivity with pore diameter (155 ± 34) μm, 91.3% ± 2.0% porosity and 2 451% ± 155% water absorption rate. The intrinsic cytotoxicity assessment of novel scaffolds using MTT test showed that the scaffolds had no cytotoxic effect on BMSCs. Inverted microscope showed that most of the cells attached to the scaffold. SEM micrographs indicated that cells covered the scaffolds uniformly and majority of the cells showed the round or ell iptic morphology with much matrix secretion. Conclusion The 3-D porous CACM scaffold reserved most of extracellular matrix after thoroughly decellularization, has good pore diameter and porosity, non-toxicity and good biocompatibil ity, which make it a suitable candidate as an alternative cell-carrier for cartilage tissue engineering.
Objective To explore an experimental method of transfecting the marrow stromal stem cells (MSCs) with the reconstructed PGL3-t ransforming growth factor-β1 (TGF-β1) gene and to evaluate the feasibility of selfinduction of MSCs to the chondrocytes in vitro so as to provide a scientific and experimental basis for a further “gene enhanced tissue engineering” research. Methods The rabbit MSCs was transfected with the reconstructed PGL3-TGF-β1gene by the Liposo mesMethod, the growth of the cells were observed, and the growth curve was drawn. The living activity of the transfected cells in the experimental group was evalua ted by MTT, and the result was significantly different when compared with that in the control group. By the immunohistochemistry method (SABC), the antigens of TGF-β1 and collagen Ⅱ were examined at 2 and 7 days of the cell culture afte r transfe ction with PGL3-TGF-β1gene. The pictures of the immunohistochemistry slice were analyzed with the analysis instrument, and the statistical analysis was perfor med with the software of the SPSS 11.0, compared with the control group and the blank group. Results Transfection of the cultured rabbit MSCs in vitro with the reconstructed PGL3-TGF-β1gene by the Liposomes Method achie ved a success, with a detection of the Luceraferase activity. The result was significantly different from that in the control group (Plt;0.01). Tested by MTT, the living acti vity of the transfected cells was proved to be significantly decreased (Plt;0.01 vs. the control group). By the immunohistochemistry method (SABC) to study TGF-β1 positive particles were detected in the experimental group，but there were no positive particles in the control and the blank groups. There was a significant difference between the two groups of the experiment and the control group based on the analysis of the ttest (Plt;0.01). By the immunohistochemistry me thod (SABC) to study collagen Ⅱ, there were more positive particles in the transfected cells in t he experimental group than in the control and the blank groups, and there was a significant difference between the experimental group and the two other groups based on the t-test (Plt;0.01). Conclusion Transfection of the rabbit MSCs with the reconstructed PGL3-TGF-β1 gene by the Liposomes Method is successful. There may be some damage to the cells when transfection is performed. The transfecte d BMS cells with PGL3-TGF-β1 gene can express and excrete TGF-β1when cultured in vitro. The transfected MSCs that secret TGF-β1 can be self-induced into the chondrocytes after being infected for 7 days when cultured in vitro.
Objective To explore the effect of tissue engineered cartilage reconstructed by using sodium alginate hydrogel and SIS complex as scaffold material and chondrocyte as seed cell on the repair of full-thickness articular cartilage defects. Methods SIS was prepared by custom-made machine and detergent-enzyme treatment. Full-thickness articularcartilage of loading surface of the humeral head and the femoral condyle obtained from 8 New Zealand white rabbits (2-3weeks old) was used to culture chondrocytes in vitro. Rabbit chondrocytes at passage 4 cultured by conventional multipl ication method were diluted by sodium alginate to (5-7) × 107 cells/mL, and then were coated on SIS to prepare chondrocyte-sodium alginate hydrogel-SIS complex. Forty 6-month-old clean grade New Zealand white rabbits weighing 3.0-3.5 kg were randomized into two groups according to different operative methods (n=20 rabbits per group), and full-thickness cartilage defect model of the unilateral knee joint (right or left) was establ ished in every rabbit. In experimental group, the complex was implanted into the defect layer by layer to construct tissue engineered cartilage, and SIS membrane was coated on the surface to fill the defect completely. While in control group, the cartilage defect was filled by sodium alginate hydrogel and was sutured after being coated with SIS membrane without seeding of chondrocyte. General condition of the rabbits after operation was observed. The rabbits in two groups were killed 1, 3, 5, 7, and 9 months after operation, and underwent gross and histology observation. Results Eight rabbits were excluded due to anesthesia death, wound infection and diarrhea death. Sixteen rabbits per group were included in the experiment, and 3, 3, 3, 3, and 4 rabbits from each group were randomly selected and killed 1, 3, 5, 7, and 9 months after operation, respectively. Gross observation and histology Masson trichrome staining: in the experimental group, SIS on the surface of the implant was fused with the host tissue, and the inferface between them disappeared 1 month after operation; part of the implant was chondrified and the interface between the implant and the host tissue was fused 3 months after operation; the implant turned into fibrocartilage 5 months after operation; fiber arrangement of the cartilage in theimplant was close to that of the host tissue 7 months after operation; cartilage fiber in the implant arranged disorderly andactive cell metabol ism and prol iferation were evident 9 months after operation. While in the control group, no repair of thedefect was observed 9 months after operation. No obvious repair was evident in the defects of the control group within 9months after operation. Histomorphometric evaluation demonstrated that the staining intensity per unit area of the reparative tissue in the defect of the experimental group was significant higher than that of the control group at each time point (P lt; 0.05), the chondrification in the experimental group was increased gradually within 3, 5, and 7 months after operation (P lt; 0.05), and it was decreased 9 months after operation comparing with the value at 7 months after operation (P lt; 0.05). Conclusion Constructed by chondrocyte-sodium alginate hydrogel-SIS in complex with surficial suturing of SIS membrane, the tissue engineered cartilage can in-situ repair cartilage defect, promote the regeneration of cartilage tissue, and is in l ine with physiological repair process of articular cartilage.
Objective To investigate the feasibility of the complex of the fibrin sealant (FS) and the bone marrow mesenchymal stem cells（MSCs） to createanew cartilage in the nude mice by the issue engineering technique. Methods T he MSCs were isolated from healthy humans and were expanded in vitro. And then the MSCs were induced by the defined medium containing the transforming growth factor β1 (TGF-β1), dexamethasone, and ascorbic acid. The biomechanical properties of the chondrocytes were investigated at 7 and 14 days. The MSCs induced for 7days were collected and mixed with FS. Then, the FSMSCs mixture was injectedby a needle into the dorsum of the nude mice in the experimental group. In the tw o control groups, only FS or MSCs were injected respectively. The specimens were harvested at 6 and 12 weeks，and the ability of chondrogenesis in vivo was inve stigated by the gross observation, HE, Alcian Blue staining, and type Ⅱ collagen immunohistochemistry. Results The MSCs changed from a spindlel ike fibroblastic appearance to a polygonal shape when transferred to the defined medium, and couldbe induced to express the chondrocyte matrix. After an injection of the mixture , the cartilage-like tissue mass was formed, and the specimens were harvested from the mass at 6 and 12 weeks in the experimental group. The tissue mass at 6 we eks was smaller and relatively firm in texture, which had a distinct lacuna structure. And glycosaminoglycan (GAG) and Type II Collagen expressions were detecte d. The tissue mass at 12 weeks was bigger, firmer and glossier with the mature c hondrocytes lying in the lacuna structure. The positive Alcian blue and Collagen II immunohistochemistry stainings were ber at 12 weeks than at 6 weeks. But there was no cartilage-like tissue mass formed in the two control groups. Conclusion This study demonstrates that the fibrin sealant and the bone marrow mesenchymal stem cells can be successfully used in a constructing technique for the tissue engineered injectable cartilage.
Objective To study the effect of platelet lysate (PL) on chondrogenic differentiation of human umbil ical cord derived mesenchymal stem cells (hUCMSCs) in vitro. Methods Umbil ical cords were voluntarily donated by healthy mothers. The hUCMSCs were isolated by collagenase digestion and cultured in vitro. The surface markers of the cells were detected by flow cytometer. According to different components of inductive medium, the cultured hUCMSCs were divided into 3 groups: group A [H-DMEM medium, 10% fetal bovine serum (FBS), and 10%PL]; group B [H-DMEM medium, 10%FBS,10 ng/mL transforming growth factor β1 (TGF-β1), 1 × 10-7 mol/L dexamethasone, 50 μg/mL Vitamin C, and 1% insul intransferrin- selenium (ITS)]; and group C (H-DMEM medium, 10%FBS, 10 ng/mL TGF-β1, 1 × 10-7mol/L dexamethasone, 50 μg/ mL vitamin C, 1%ITS, and 10%PL). The hUCMSCs were induced in the mediums for 2 weeks. Toluidine blue staining was used to detect the secretion of chondrocyte matrix. Immunofluorescence method was used to identify the existence of collagen trpe II. The expressions of Aggrecan and collagen type II were detected by semiquantitative RT-PCR. Results Flow cytometer results showed that the hUCMSCs did not express the surface markers of hematopoietic cell CD34, CD45, and human leukocyte antigen DR, but expressed the surface markers of adhesion molecule and mesenchymal stem cells CD44, CD105, and CD146. Toluidine blue staining and immunofluorescence showed positive results in group C, weak positive results in group B, and negative results in group A. Semiquantitative RT-PCR showed the expressions of Aggrecan and collagen type II at mRNA level in groups B and C, but no expression in group A. The mRNA expressions of Aggrecan and collagen type II were higher in group C than in group B (P lt; 0.05). Conclusion Only 10%PL can not induce differentiation of hUCMSCs into chondrocytes, but it can be a supplement to the induced mediums. PL can improve hUCMSCs differentiating into chondrocytes obviously in vitro. This study provides new available conditions for constructing tissue engineered cartilage.
To study how to repair the cartilage defect according to the principles of tissue engineering with acellular cartilage matrix as scaffold material. Methods The ear cartilage was obtained from a New Zealand white rabbit(weighing 2.4 kg )and then treated by a modified Courtman’s four-step method to produce the acellular cartilage matrix. Eighteen New Zealand white rabbits (aged 6 months, weighing 2.4-2.6 kg) with no sex l imit were divided into three groups. Forevery rabbit, two pieces of ear cartilage measured 1 cm × 1 cm were excised in each ear. Defects were repaired as follows: group A with the combined graft of acellular cartilage matrix and perichondium, group B with acellular cartilage matrix and group C with perichondium. Three animals in each group were killed 4 and 12 weeks postoperatively, respectively. Tissue samples obtained were analyzed with gross observation, hematoxyl in-eosin stain, Safranine O-alcian blue stain and type II collagen messenger RNA in situ hybridization respectively. Results In gross observation, the repaired sites in groups A and B were not change meaningfully in their shape 4 weeks postoperatively; but they felt a bit of thicker and harder 12 weeks postoperatively. In group C two repaired sites formed scabs at 2 weeks and perforated at 5 weeks. In histological observation, there was a sl ight inflammatory reaction surrounding the acellular cartilage matrix 4 weeks after it was implanted in groups A and B. The inflammatory cells were mainly lymphocytes. The perichondrium graft in group C was collapsed in the defects in HE stain. The defect sites were negative for Safranine O-alcian blue stain and type II collagen mRNA in situ hybridization in all groups. At 12 weeks cells were found in the acellular matrix which arranged in irregular manner in group A in HE stain and was positive for Safranine O-alcian blue stain and type II collagen mRNA in site hybridization. In groups B and C, no new cell was found in HE stain and the repaired sites were negative for Safranine O-alcian blue stain and type II collagen mRNA in situ hybridization. Conclusion Acellular
ObjectiveTo explore the feasibility of three-dimensional (3D) bioprinted adipose-derived stem cells (ADSCs) combined with gelatin methacryloyl (GelMA) to construct tissue engineered cartilage.MethodsAdipose tissue voluntarily donated by liposuction patients was collected to isolate and culture human ADSCs (hADSCs). The third generation cells were mixed with GelMA hydrogel and photoinitiator to make biological ink. The hADSCs-GelMA composite scaffold was prepared by 3D bioprinting technology, and it was observed in general, and observed by scanning electron microscope after cultured for 1 day and chondrogenic induction culture for 14 days. After cultured for 1, 4, and 7 days, the composite scaffolds were taken for live/dead cell staining to observe cell survival rate; and cell counting kit 8 (CCK-8) method was used to detect cell proliferation. The composite scaffold samples cultured in cartilage induction for 14 days were taken as the experimental group, and the composite scaffolds cultured in complete medium for 14 days were used as the control group. Real-time fluorescent quantitative PCR (qRT-PCR) was performed to detect cartilage formation. The relative expression levels of the mRNA of cartilage matrix gene [(aggrecan, ACAN)], chondrogenic regulatory factor (SOX9), cartilage-specific gene [collagen type Ⅱ A1 (COLⅡA1)], and cartilage hypertrophy marker gene [collagen type ⅩA1 (COLⅩA1)] were detected. The 3D bioprinted hADSCs-GelMA composite scaffold (experimental group) and the blank GelMA hydrogel scaffold without cells (control group) cultured for 14 days of chondrogenesis were implanted into the subcutaneous pockets of the back of nude mice respectively, and the materials were taken after 4 weeks, and gross observation, Safranin O staining, Alcian blue staining, and collagen type Ⅱ immunohistochemical staining were performed to observe the cartilage formation in the composite scaffold.ResultsMacroscope and scanning electron microscope observations showed that the hADSCs-GelMA composite scaffolds had a stable and regular structure. The cell viability could be maintained at 80%-90% at 1, 4, and 7 days after printing, and the differences between different time points were significant (P<0.05). The results of CCK-8 experiment showed that the cells in the scaffold showed continuous proliferation after printing. After 14 days of chondrogenic induction and culture on the composite scaffold, the expressions of ACAN, SOX9, and COLⅡA1 were significantly up-regulated (P<0.05), the expression of COLⅩA1 was significantly down-regulated (P<0.05). The scaffold was taken out at 4 weeks after implantation. The structure of the scaffold was complete and clear. Histological and immunohistochemical results showed that cartilage matrix and collagen type Ⅱ were deposited, and there was cartilage lacuna formation, which confirmed the formation of cartilage tissue.ConclusionThe 3D bioprinted hADSCs-GelMA composite scaffold has a stable 3D structure and high cell viability, and can be induced differentiation into cartilage tissue, which can be used to construct tissue engineered cartilage in vivo and in vitro.
Objective To study the influence of different mechanical environments on repair cartilage defect with marrow mesenchymal stem cells as seed cells. Methods The rabbit marrow mesenchymal stem cells were isolated and cultured. The cartilage defects were repaired by autologous tissue engineered cartilage with the marrow mesenchymal stem cells as seed cells. Fifteen rabbits with cartilage defect were divided into 3 groups: dislocation group with cell-free scaffold(controlgroup), dislocation group with cartilaginous construct and normal mechanical environment group with cartilaginous construct. The repaired tissue was harvested and examined 6 weeks postoperatively. Results The repair tissue in normal mechanical environment group with cartilaginous construct showed cartilage-like tissue in superficial layer and subchondral bone tissue in deep layer 6 weeks postoperatively. The defect was filled with bone tissue in dislocation group with cartilaginous construct 6 weeks postoperatively. The surrounding normal cartilage tissue showed vascular invasion from subchondral area and the concomitant thinningof the normal cartilage layer. The cartilaginous construct left in the femoral trochlea groove formed hyaline cartilage-like tissue. The defect was repaired byfibrous tissue in control group. Conclusion The repaired tissue by tissue engineered cartilage with marrow mesenchymal stem cells as seed cells showed the best result in normal mechanical environment group, which indicates that it will be essential for the formation and maintenance of tissue engineered cartilage to keep the normal mechanical stress stimulus.
Objective To investigate the effect of “two-phase” tissue engineered cartilage constructed by autologous marrow mesenchymal stem cells(MSCs) and allogeneic bone matrix gelatin(BMG) in repairing articular cartilage defects. Methods Thirty-twoNew Zealand white rabbits were involved in the experiment. “Two-phase” allogeneic BMG scaffold (one side of porous cancellous bone and the other side of cortical bone; 3 mm both in diameter and in thickness) was prepared from iliac bone and limb bone of 5 rabbits by sequentially chemical method. The MSCs wereseparated from 18 New Zealand white rabbits and induced to express chondrocyticphenotype. The chondrocyte precursor cells were seeded onto “two-phase” allogeneic BMG to construct tissue engineering cartilage. Masson’s trichrome staining, PAS staining and scanning electronic microscopic observation were carried out at 1, 3 and 5 weeks. The defects of full thickness articular cartilage(3 mm both in diameter and in depth) were made at both sides of femoral medial condyles in 27 rabbits(including 18 of separated MSCs and the remaining 9). The defects were repaired with the tissue engineered cartilage at the right side (group A, n=18), with BMG at the left side(group B, n=18), and without any implant at both sides in the remaining 9 rabbits as a control( group C, n=18). After 1, 3 and6 months, the 6 specimens of femoral condyles were harvested in 3 groups, respectively. Gross observation, Masson’s trichrome and Alcian blue staining, modified Wakitani scoring and in situ hybridization of collagen type Ⅱ were carried out to assess the repair efficacy of tissue engineered cartilage. Results The “two-phase” BMG consisted of the dense cortical part and the loose cancellous part. In cancellous part, the pore size ranged 100-800 μm, in which the chondrocyte precursor cells being induced from MSCs proliferated and formed the cell-rich cartilaginous part of tissue engineered cartilage. In cortical part, the pore size ranged 10-40 μm, on which the cells arranged in a layer and formed the hard part of subchondral bone. After 1 month of transplantation, the cartilage and subchondral bone were regenerated in group A; during observation, the regenerated cartilage graduallythinned, but defect was repaired and the structure of the articular surface ansubchondral bone was in integrity. In groups B and C, defects were not repaired, the surrounding cartilage of defect was abrased. According to the modified Wakitani scoring, the indexes in group A were significantly higher than those in group B and C(Plt;0.01) except the thickness of cartilage at 6 months. The positive cell rate of in situ hybridization for collagen type Ⅱ in group A was also higher than those in groups B and C(Plt;0.01). Conclusion “Two-phase” allogeneic BMG is a prospective scaffold for tissue engineered cartilage,which combines with autologous chondrocyte precursor cells induced from MSCs toconstruct the tissue engineering cartilage. The tissue engineered cartilage can repair defects of articular cartilage and subchondral bone.