Objective To research in vitro biocompatibility of silicon containing micro-arc oxidation (MAO) coated magnesium alloy ZK60 with osteoblasts. Methods The surface microstructure of silicon containing MAO coated magnesium alloy ZK60 was observed by a scanning electron microscopy (SEM), and chemical composition of the coating surface was determined by energy dispersive spectrum analysis. The experiments were divided into 4 groups: silicon containing MAO coated magnesium alloy ZK60 group (group A), uncoated magnesium alloy ZK60 group (group B), titanium alloy group (group C), and negative control group (group D). Extracts were prepared respectively with the surface area to extraction medium ratio (1.25 cm2/ mL) according to ISO 10993-12 standard in groups A, B, and C, and were used to culture osteoblasts MC3T3-E1. The α-MEM medium supplemented with 10% fetal bovine serum was used as negative control in group D. The cell morphology was observed by inverted phase contrast microscopy. MTT assay was used to determine the cell viability. The activity of alkaline phosphatase (ALP) was detected. Cell attachment morphology on the surface of different samples was observed by SEM. The capability of protein adsorption of the coating surface was assayed, then DAPI and calcein-AM/ethidium homodimer 1 (calcein-AM/EthD-1) staining were carried out to observe cell adhesion and growth status. Results The surface characterization showed a rough and porous layer with major composition of Mg, O, and Si on the surface of silicon containing MAO coated magnesium alloy ZK60 by SEM. After cultured with the extract, cells grew well and presented good shape in all groups by inverted phase contrast microscopy, group A was even better than the other groups. At 5 days, MTT assay showed that group A presented a higher cell proliferation than the other groups (P lt; 0.05). Osteoblasts in groups A and C presented a better cell extension than group B under SEM, and group A exhibited better cell adhesion and affinity. Protein adsorption in group A [ (152.7 ± 6.3) µg/mL] was significantly higher than that of group B [(96.3 ± 3.9) µg/mL] and group C [ (96.1 ± 8.7) µg/mL] (P lt; 0.05). At each time point, the adherent cells on the sample surface of group A were significantly more than those of groups B and C (P lt; 0.05). The calcein-AM/EthD-1 staining showed that groups A and C presented better cell adhesion and growth status than group B. The ALP activities in groups A and B were 15.55 ± 0.29 and 13.75 ± 0.44 respectively, which were significantly higher than those in group C (10.43 ± 0.79) and group D (10.73 ± 0.47) (P lt; 0.05), and group A was significantly higher than group B (P lt; 0.05). Conclusion The silicon containing MAO coated magnesium alloy ZK60 has obvious promoting effects on the proliferation, adhesion, and differentiation of osteoblasts, showing a good biocompatibility, so it might be an ideal surface modification method on magnesium alloys.
Objective To evaluate the effectiveness of biodegradable magnesium alloy materials in promoting tendon-bone healing during rotator cuff tear repair and to investigate their potential underlying biological mechanisms. Methods Forty-eight 8-week-old Sprague Dawley rats were taken and randomly divided into groups A, B, and C. Rotator cuff tear models were created and repaired using magnesium alloy sutures in group A and Vicryl Plus 4-0 absorbable sutures in group B, while only subcutaneous incisions and sutures were performed in group C. Organ samples of groups A and B were taken for HE staining at 1 and 2 weeks after operation to evaluate the safety of magnesium alloy, and specimens from the supraspinatus tendon and proximal humerus were harvested at 2, 4, 8, and 12 weeks after operation. The specimens were observed macroscopically at 4 and 12 weeks after operation. Biomechanical tests were performed at 4, 8, and 12 weeks to test the ultimate load and stiffness of the healing sites in groups A and B. At 2, 4, and 12 weeks, the specimens were subjected to the following tests: Micro-CT to evaluate the formation of bone tunnels in groups A and B, HE staining and Masson staining to observe the regeneration of fibrocartilage at the tendon-bone interface after decalcification and sectioning, and Goldner trichrome staining to evaluate the calcification. Immunohistochemical staining was performed to detect the expression of angiogenic factors, including vascular endothelial growth factor (VEGF) and bone morphogenetic protein 2 (BMP-2), as well as osteogenic factors at the tendon-bone interface. Additionally, immunofluorescence staining was used to examine the expression of arginase 1 and Integrin beta-2 to assess M1 and M2 macrophage polarization at the tendon-bone interface. The role of the phosphatidylinositol 3-kinase (PI3K)/protein kinase B (AKT) signaling pathway in tendon-bone healing was further analyzed using real-time fluorescence quantitative PCR. Results Analysis of visceral sections revealed that magnesium ions released during the degradation of magnesium alloys did not cause significant toxic effects on internal organs such as the heart, liver, spleen, lungs, and kidneys, indicating good biosafety. Histological analysis further demonstrated that fibrocartilage regeneration at the tendon-bone interface in group A occurred earlier, and the amount of fibrocartilage was significantly greater compared to group B, suggesting a positive effect of magnesium alloy material on tendon-bone interface repair. Additionally, Micro-CT analysis revealed that bone tunnel formation occurred more rapidly in group A compared to group B, further supporting the beneficial effect of magnesium alloy on bone healing. Biomechanical testing showed that the ultimate loads in group A were consistently higher than in group B, at 4 weeks, the stiffness of group A was also greater than that of group B, indicating stronger tissue-carrying capacity following tendon-bone interface repair and highlighting the potential of magnesium alloy in enhancing tendon-bone healing. Immunohistochemical staining results indicated that the expression of VEGF and BMP-2 was significantly upregulated during the early stages of healing, suggesting that magnesium alloy effectively promoted angiogenesis and bone formation, thereby accelerating the tendon-bone healing process. Immunofluorescence staining further revealed that magnesium ions exerted significant anti-inflammatory effects by regulating macrophage polarization, promoting their shift toward the M2 phenotype. Real-time fluorescence quantitative PCR results demonstrated that magnesium ions could facilitate tendon-bone healing by modulating the PI3K/AKT signaling pathway, which represented one of the molecular mechanisms driving this healing process. ConclusionBiodegradable magnesium alloy material accelerated fibrocartilage regeneration and calcification at the tendon-bone interface in rat rotator cuff tear repair by regulating the PI3K/AKT signaling pathway, thereby significantly enhancing tendon-bone healing.